Rotor ve Stator Yığınlarının Çekirdek Üretimi
|
0,35 mm |
25SWYS500 |
|---|---|
|
0,50 mm |
35SWYS500 / 35SWYS600 / 35SWYS900 |
|
0,65 mm |
50SWYS650 |
|
Uygulama |
65SWYS600 |
Manyetik Özellikler ve Mekanik Özellikler
|
Uygulama etkisi |
New energy vehicle high-speed drive motor rotor. |
|---|---|
|
Motorlarda Manyetik Uygulamalar İçin Daha Yüksek Mukavemetli Çelikler |
The yield strength reaches 950MPa, which is 150MPa higher than the highest yield strength of electrical steel in the world. |
|
Ürün avantajları |
By using Shougang 35SWYS900 non-oriented electrical steel products, the motor torque increased by 11.3% and the maximum efficiency point increased by 0.7%. |
Seri sınıfları
| Grades | Core loss P1.0/400(W/kg) |
Magnetic induction B50(T) |
Hardness (HV1) |
Yield strength (MPa) |
Tensile strength (MPa) |
|---|---|---|---|---|---|
| 35SWYS600 | 38.0 | 1.63 | 235 | 615 | 685 |
| 35SWYS900 | 60.0 | 1.54 | 300 | 940 | 960 |